Stainless Steel Pipe

We are committed to providing our customers with top-notch Stainless Steel Pipe Suppliers in Mumbai that meet their specific requirements. With our extensive product range, impeccable quality standards, and customer-centric approach, we have become a trusted name in the industry.

There are different types and sizes available in ss pipes. The Stainless Steel ERW Pipe is electric resistance welded whereas the other types such as electric fusion welded and cold drawn pipes are also available.

Specification


Outside Diameter

10.3 mm to 762 mm

Wall Thickness

Schedule 5S up to SCH XXS

Grades

ASTM A312 TP304
ASTM A312 TP304L
ASTM A312 TP316
ASTM A312 TP316L
ASTM A312 TP321
ASTM A312 TP321H
ASTM A312 TP347H
ASTM A312 TP347
ASTM A312 TP310S
ASTM A312 TP304H
Stainless Steel 410 Pipe
Stainless Steel 317L Pipe
Stainless Steel 310 Pipe
Stainless Steel 316H Pipe

Standard

ASME B36.19, ASME B36.19M

Applications

General Service,Drinking water, Hydraulic Power system, Marine, Food & Dairy sector, Oil & Gas industries

Shape

Round/ Cylindrical, Square, Rectangular

Products Range


Chemical Composition


Grade Mark Chemical Compositions(%)
C Cr Ni Mn P S Mo Si Cu N Others
201 1Cr17Mn
6Ni5N		 ≤0.15 16.00-
18.00		 3.50-
5.50		 5.50－
7.50		 ≤0.060 ≤0.03 - ≤1.00 - ≤0.25 -
201L 03Cr17Mn
6Ni5N		 ≤0.03 16.00-
18.00		 3.50-
5.50		 5.50－
7.50		 ≤0.060 ≤0.03   ≤1.00   ≤0.25  
202 1Cr18Mn
8Ni5N		 ≤0.15 17.00-
19.00		 4.00-
6.00		 7.50-
10.00		 ≤0.060 ≤0.03   ≤1.00 - ≤0.25 -
204 03Cr16Mn
8Ni2N		 ≤0.03 15.00-
17.00		 1.50-
3.50		 7.00-
9.00		           0.15-
0.30		  
China 1Cr18Mn10Ni
5Mo3N		 ≤0.10 17.00-
19.00		 4.00-
6.00		 8.50-
12.00		     2.8-
3.5		     0.20-
0.30		  
Russia 2Cr13Mn
9Ni4		 0.15-
0.25		 12.00-
14.00		 3.70-
5.00		 8.00-
10.00		              
China 2Cr15Mn
15Ni2N		 0.15-
0.25		 14.00-
16.00		 1.50-
3.00		 14.00-
16.00		           0.15-
0.30		  
  1Cr18Mn
10Ni5Mo3N		 ≤0.15 17.00-
19.00		 4.00-
6.00		 8.50-
12.00		 ≤0.060 ≤0.03 2.8-
3.5		 ≤1.00 - 0.20-
0.30		 -
301 1Cr17Ni7 ≤0.15 16.00-
18.00		 6.00-
8.00		 ≤2.00 ≤0.065 ≤0.03 - ≤1.00 - - -
302 1Cr18Ni9 ≤0.15 17.00-
19.00		 8.00-
10.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - - -
303 Y1Cr18Ni9 ≤0.15 17.00-
19.00		 8.00-
10.00		 ≤2.00 ≤0.20 ≤0.03 1) ≤1.00 - - -
303se Y1Cr18Ni
9Se		 ≤0.15 17.00-
19.00		 8.00-
10.00		 ≤2.00 ≤0.20 ≤0.03 - ≤1.00 - - Se≥0.15
304 0Cr18Ni9 ≤0.07 17.00-
19.00		 8.00-
10.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - - -
304L 00Cr19Ni10 ≤0.03 18.00-
20.00  		 8.00-
10.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - - -
304N1 0Cr19Ni9N ≤0.08 18.00-
20.00  		 7.00-
10.50		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - 0.10-
0.25		 -
304N2 0Cr18Ni
10NbN		 ≤0.08 18.00-
20.00  		 7.00-
10.50		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - 0.15-
0.30		 Nb≤0.15
304LN 00Cr18Ni
10N		 ≤0.03 17.00-
19.00		 8.50-
11.50		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - 0.12-
0.22		 -
305 1Cr18Ni12 ≤0.12 17.00-
19.00		 10.50-
13.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 -   -
309S 0Cr23Ni13 ≤0.08 22.00-
24.00		 12.00-
15.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 -   -
310S 0Cr25Ni20 ≤0.08 24.00-
26.00		 19.00-
22.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - - -
316 0Cr17Ni
12Mo2		 ≤0.08 16.00-
18.50		 10.00-
14.00		 ≤2.00 ≤0.035 ≤0.03 2.00-
3.00		 ≤1.00 - - -
  1Cr18Ni
12Mo2Ti6)		 ≤0.12 16.00-
19.00		 10.00-
14.00		 ≤2.00 ≤0.035 ≤0.03 1.80-
2.50		 ≤1.00 - - Ti5
(C%-0.02)~
0.08
  0Cr18Ni
12Mo2Ti		 ≤0.08 16.00-
19.00		 10.00-
14.00		 ≤2.00 ≤0.035 ≤0.03 1.80-
2.50		 ≤1.00 - - Ti5*C%-
0.70
316L 00Cr17Ni
14Mo2		 ≤0.03 16.00-
18.00		 12.00-
15.00		 ≤2.00 ≤0.035 ≤0.03 2.00-
3.00		 ≤1.00 - - -
316N 0Cr17Ni
12Mo2N		 ≤0.08 16.00-
18.00		 10.00-
14.00		 ≤2.00 ≤0.035 ≤0.03 2.00-
3.00		 ≤1.00 - - -
316N 00Cr17Ni
13Mo2N		 ≤0.03 16.00-
18.50		 10.50-
14.50		 ≤2.00 ≤0.035 ≤0.03 2.00-
3.00		 ≤1.00 - - -
316J1 0Cr18Ni
12Mo2Cu2		 ≤0.08 17.00-
19.00		 10.50-
14.50		 ≤2.00 ≤0.035 ≤0.03 1.20-
2.75		 ≤1.00 1.00-
2.50		 - -
316J1L 00Cr18Ni
14Mo2Cu2		 ≤0.03 17.00-
19.00		 12.00-
16.00		 ≤2.00 ≤0.035 ≤0.03 1.20-
2.75		 ≤1.00 1.00-
2.50		 - -
317 0Cr19Ni
13Mo3		 ≤0.12 18.00-
20.00		 11.00-
15.00		 ≤2.00 ≤0.035 ≤0.03 3.00-
4.00		 ≤1.00 - - -
317L 00Cr19Ni
13Mo3		 ≤0.08 18.00-
20.00		 11.00-
15.00		 ≤2.00 ≤0.035 ≤0.03 3.00-
4.00		 ≤1.00 - - -
  1Cr18Ni
12Mo3Ti6		 ≤0.12 16.00-
19.00		 11.00-
14.00		 ≤2.00 ≤0.035 ≤0.03 2.50-
3.50		 ≤1.00 - - Ti5
(C%-0.02)~
0.08
  0Cr18Ni
12Mo3Ti		 ≤0.08 16.00-
19.00		 11.00-
14.00		 ≤2.00 ≤0.035 ≤0.03 2.50-
3.50		 ≤1.00 - - Ti5*C%-
0.70
317J1 0Cr18Ni
16Mo5		 ≤0.04 16.00-
19.00		 15.00-
17.00		 ≤2.00 ≤0.035 ≤0.03 4.00-
6.00		 ≤1.00 - - -
321 1Cr18Ni9Ti6) ≤0.12 17.00-
19.00		 8.00-
11.00		 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - Ti5
(C%-0.02)~
0.08
  0Cr18Ni10Ti ≤0.08 17.00-
19.00		 9.00-
12.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - - Ti≥5*C%
347 0Cr18Ni11Nb ≤0.08 17.00-
19.00		 9.00-
13.00		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 - - Nb≥10*C%
XM7 0Cr18Ni9Cu3 ≤0.08 17.00-
19.00		 8.50-
10.50		 ≤2.00 ≤0.035 ≤0.03 - ≤1.00 3.00-
4.00		 - -
XM15J1 0Cr18Ni13Si4 ≤0.08 15.00-
20.00		 11.50-
15.00		 ≤2.00 ≤0.035 ≤0.03 - 3.00-
5.00		   - 2

Mechanical Composition


MECHANICAL PROPERTIES
Grade Tensile
Strength Mpa, (Min)		 Yield
Strength
Mpa, (Min)		 %Age
Elongation
in 50mm
gauge length min		 Hardness (Max)
BHN Rb
301 515 205 40 217 95
304 515 205 40 201 92
304L 485 170 40 201 92
310S 515 205 40 217 95
316 515 205 40 217 95
316L 485 170 40 217 95
317 515 205 35 217 95
317L 515 205 40 217 95
321 515 205 40 217 95
347 515 205 40 201 92
409 380 170 20 179 88
409M 430 275 20 187 90
410S 415 205 22 183 89
410 450 205 20 217 89
420 700( max ) - 15 217 95
430 450 205 22 183 89
JSL AUS 515 205 40 217 95
JS- 203 515 205 40 217 95
301M 515 205 40 217 95